Quote:
Originally Posted by TopgunZ
Nylon is nice. Thats what I am using. It flexes some if you need it. I added in the glass fill so it can withstand even higher temps. PCarb is going to be super rigid and brittle but strong as hell. Its all application specific I guess.
|
For your cannon intake? I know you said you don’t think there are any 3D materials that will stand up to the heat and cold over a long time.